Speed-sintering zirconia
SPEED
Designed for shorter sintering workflows while balancing strength, translucency and dimensional stability.
Technical data
Complete
specifications.
Material properties, composition and product positioning published for the SPEED family.
- Product type
- Speed-sintering zirconia
- Yttria composition
- 4 mol%
- Fracture toughness
- 4.5
- Sintering temperature
- 1500°C
- Density
- ≥ 6.0 g/cm³
- Chemical solubility
- ≤ 100 µg/cm²
- Radioactivity
- < 0.1 Bq/g
- ZrO₂ + HfO₂ + Y₂O₃
- > 99 wt%
- Other oxides
- ≤ 1.0 wt%
Formats & shades
Every available
configuration.
Open-system Ø98 mm discs with the thickness and shade choices published for this family.
Open-system disc
Thicknesses
Shade range
Sintering workflow
Published programs
and temperature curves.
Review each stage and its corresponding Matovix chart. Use the batch instructions and a calibrated furnace for production.
- 01
Standard cycle: 1500°C peak; approximately 504 minutes
- 02
Single crown: 20°C → 1150°C at 200°C/min → 1300°C at 30°C/min → 1400°C at 20°C/min → 1500°C at 30°C/min; hold 10 minutes; total 29 minutes
- 03
Up to 3-unit bridge: 20°C → 1250°C at 50°C/min → 1500°C at 12°C/min; hold 20 minutes; total 75 minutes
- 04
3–6 unit bridge: 20°C → 1050°C at 50°C/min → 1530°C at 5°C/min; hold 60 minutes; cool to 800°C at 38°C/min; total 197 minutes
Indications
Where SPEED
fits the workflow.
Single crowns and bridges from one to six units using the appropriate published rapid or standard cycle.
Values, shade availability and charts are based on Matovix's current published information. Final product, batch protocol and indication should be confirmed before use.