High-strength multilayer zirconia
SOLID Multi
A multilayer option developed around the SOLID family for high-strength restorative workflows.
Matovix currently routes SOLID Multi to the SOLID technical source. The page below separates the multilayer product while retaining the published SOLID-family technical information; the exact batch protocol is confirmed before supply.
Technical data
Complete
specifications.
Material properties, composition and product positioning published for the SOLID Multi family.
- Product type
- High-strength multilayer zirconia
- Yttria composition
- 3 mol%
- Fracture toughness
- 5.5
- Sintering temperature
- 1500°C
- Density
- ≥ 6.0 g/cm³
- Chemical solubility
- ≤ 100 µg/cm²
- Radioactivity
- < 0.1 Bq/g
- ZrO₂ + HfO₂ + Y₂O₃
- > 99 wt%
- Other oxides
- ≤ 1.0 wt%
Formats & shades
Every available
configuration.
Open-system Ø98 mm discs with the thickness and shade choices published for this family.
Open-system disc
Thicknesses
Shade range
Sintering workflow
Published programs
and temperature curves.
Review each stage and its corresponding Matovix chart. Use the batch instructions and a calibrated furnace for production.
- 01
Room temperature → 1150°C at 8°C/min; hold 30 minutes
- 02
1150°C → 1300°C at 2°C/min
- 03
1300°C → 1500°C at 4°C/min; hold 120 minutes
- 04
Cool to 800°C at 8°C/min
- 05
Published total cycle: approximately 504 minutes
Indications
Where SOLID Multi
fits the workflow.
High-strength multilayer restorations. Matovix currently references the SOLID technical family; the exact batch protocol is confirmed before supply.
Values, shade availability and charts are based on Matovix's current published information. Final product, batch protocol and indication should be confirmed before use.