Medium-translucent zirconia
BASE
High opacity and high strength for frameworks and implant-supported restorative structures.
Technical data
Complete
specifications.
Material properties, composition and product positioning published for the BASE family.
- Product type
- Medium-translucent zirconia
- Yttria composition
- 3 mol%
- Fracture toughness
- 6.0
- Sintering temperature
- 1500°C
- Density
- ≥ 6.0 g/cm³
- Chemical solubility
- ≤ 100 µg/cm²
- Radioactivity
- < 0.1 Bq/g
- ZrO₂ + HfO₂ + Y₂O₃
- > 99 wt%
- Other oxides
- ≤ 1.0 wt%
Formats & shades
Every available
configuration.
Open-system Ø98 mm discs with the thickness and shade choices published for this family.
Open-system disc
Thicknesses
Shade range
Sintering workflow
Published programs
and temperature curves.
Review each stage and its corresponding Matovix chart. Use the batch instructions and a calibrated furnace for production.
- 01
Room temperature → 500°C at 4°C/min
- 02
500°C → 1150°C at 8°C/min; hold 30 minutes
- 03
1150°C → 1300°C at 2°C/min
- 04
1300°C → 1500°C at 4°C/min; hold 120 minutes
- 05
Cool to 800°C at 8°C/min
- 06
Published total cycle: approximately 564 minutes
Indications
Where BASE
fits the workflow.
High-opacity implant frameworks, posterior coping structures and other support-focused restorations.
Values, shade availability and charts are based on Matovix's current published information. Final product, batch protocol and indication should be confirmed before use.